RESILIENT FLOORING ADHESIVE GUIDE
ROBERTS 12 Acrylic Sheet Vinyl Adhesive Low Odour
Composition: Acrylic Solids: Approx 68% Tackup: 10-15 minutes at 20°C **
USE: Formulated for use with both commercial, domestic plasticised, and foam backed homogenous sheet floor and wall coverings and vinyl plank vinyl floor coverings. Also suitable for bonding PVC backed carpets.ROBERTS 12SF Solvent Free Low Odour
Universal Sheet Vinyl Adhesive
Composition: Acrylic Solids: Approx 63% Tack-up: 10-15 minutes at 20°C **
USE: Provides high cohesive strength and heat resistance for bonding commercial and domestic PVC sheet flooring Roberts 12SF offers excellent resistance to plasticiser migration.ROBERTS 18 Conductive Vinyl Adhesive Low Odour
Composition: Acrylic Solids: Approx 62% Tack-up: Refer Technical Data Sheet
USE: An acrylic, water based, carbon filled adhesive, specifically formulated for the installation of conductive vinyl sheet and tile floorcoverings.Ideal for unsupported conductive, static dissipative, and some antistatic commercial vinyls.ROBERTS 21 Carpet & Vinyl Multipurpose Adhesive
Composition: Synthetic Acrylic Solids: Approx 69% Tack-up: 15-20 minutes **
USE: A non-flammable adhesive for use with most types of carpets and including foam back,
vinyl and cork.
Roberts 21 is not recommended for use with linoleum.ROBERTS 70 Rubber Flooring Adhesive Low Odour
Composition: S.B.R. Latex
Solids: Approx 62% Tack-up: 10-15 minutes at 20°C **
USE: For adhering sanded backed rubber tiles and sheet flooring goods in non-adverse conditions and commercial areas not subject to heavy maintenance.ROBERTS 101S Skirting Contact Adhesive
Composition: Neoprene Synthetic Rubber Solids: 22% Approx
Tack-up: 5-10 minutes at 20°C **
USE: Roberts 101S Skirting Contact Adhesive is a specifically formulated solvent based, rapid drying contact cement with high strength, excellent ageing and heat resistance. It is designed for use on most vinyl and plastic skirtings, coverstrips, plastic and metal treads and nosings etc.ROBERTS 114 Linoleum Adhesive
Composition: Synthetic Latex Solids: Approx 72% Tack-up: 10-15 minutes **
USE: Specifically formulated for the installation of linoleum. It has high initial grab and is ideal for bonding both sheet and tile goods.ROBERTS 121 Water Based Contact Adhesive
Composition: Acrylic
Solids: Approx 50% Tack-up: 10-15 minutes at 20°C **
USE: For bonding skirting and other PVC extrusions.ROBERTS 290 Solvent Free Low Odour Wall Vinyl & Fabric Adhesive
Composition: Acrylic Solids: Approx 73%
Tack-up: 15 minutes
USE: This adhesive has been developed especially for adhering wall vinyls and wall fabrics
in indoor applications.The adhesive may be applied using a long nap roller and it develops a soft
tacky film which may be heat reactivated to help remove bubbles.The adhesive film offers excellent rebond qualities.ROBERTS 370 Floor & Wall Primer Low Odour
Composition: Acrylic Solids: Approx 6.5%
USE: Roberts recommend the use of 370 Floor & Wall Primer on absorbent floor & wall surfaces such as concrete, hardplaster, plaster board and cement sheet to help reduce the absorption of adhesive into the substrate and settle any dust.ROBERTS 555 2 Part Flexible Polyurethane Adhesive System
Solids: Approx 100% Cure time: 10-12 hours at 20° C
USE: Specifically formulated water resistant adhesive for use on rubber flooring, commercial sheet vinyl and other difficult to hold products to concrete, brick, fibre cement sheeting, aluminium and steel.ROBERTS 570 Water Based Epoxy Sealer, Grey & Clear
Composition: Part A: Epoxy Resin Part B: Polyamine Adduct
Solids: Refer Product Data Sheet
Appearance: Refer Product Data Sheet
USE: A two-part water based epoxy primer sealer for concrete, masonry, fibrocement and other cementitious surfaces.ROBERTS 656 Solvent Free Pressure Sensitive Adhesive Low Odour
Composition: Acrylic Solids: Approx 51%
Tack-up: Approx 2-4 hours**
USE: Roberts 656 is a solvent free pressure sensitive adhesive usually used in "dry mode" for installing reinforced vinyl composition tiles. It has high cohesive strength which ensures long term performance of the adhesive.RL 1017 Polyurethane Adhesive
Composition: Polyurethane Solids: Approx 100%
Cure time: 5-7 hours but no heavy traffic for 24 hours.
USE: Is a TDI free adhesive specifically formulated for the installation of both block and mosaic parquetry. Also suitable for laminated wood flooring systems.ROBERTS 5601 Vinyl Seam Adhesive
Composition: Synthetic Resins Solids: Approx 21%
USE: Roberts 5601 is a specifically formulated non-yellowing solvent based solution for chemically welding sheet vinyl flooring.
When fully cured it forms a water resistant and flexible film.** Tack-up time is always dependent upon the type and volume of adhesive used, substrate temperature and porosity, air temperature, humidity and ventilation.
Further information on these and other Roberts products can be obtained by visiting www.rlapolymers.com.au